Graphite Electrodes With Nipples For EAF Steel Making RP Dia300X1800mm

Short Description:

RP graphite electrode is a widely used product that provides significant benefits to the steel industry. It has a low resistance, which results in low consumption of energy during the smelting process. This characteristic helps to reduce costs and increase efficiency, making it a highly cost-effective product.


Product Detail

Product Tags

Technical Parameter

Parameter

Part

Unit

RP 300mm(12”) Data

Nominal Diameter

Electrode

mm(inch)

300(12)

Max Diameter

mm

307

Min Diameter

mm

302

Nominal Length

mm

1600/1800

Max Length

mm

1700/1900

Min Length

mm

1500/1700

Max Current Density

KA/cm2

14-18

Current Carrying Capacity

A

10000-13000

Specific Resistance

Electrode

μΩm

7.5-8.5

Nipple

5.8-6.5

Flexural Strength

Electrode

Mpa

≥9.0

Nipple

≥16.0

Young’s Modulus

Electrode

Gpa

≤9.3

Nipple

≤13.0

Bulk Density

Electrode

g/cm3

1.55-1.64

Nipple

≥1.74

C.T.E.

Electrode

×10-6/℃

≤2.4

Nipple

≤2.0

Ash Content

Electrode

%

≤0.3

Nipple

≤0.3

NOTE:Any specific requirement on dimension can be offered.

Widely Application

RP graphite electrode is commonly used in LF (Ladle furnace) and EAF (Electric Arc Furnace) steelmaking. The electrode is highly compatible with these furnaces and provides excellent results. RP graphite electrode is also used in other applications like pre-baked anode and steel ladle.

Instruction For Handing And Using

1.Remove the protective cover of the new electrode hole, check whether the thread in the electrode hole is complete and the thread is incomplete, contact the professional engineers to determine whether the electrode can be used;
2.Screw the electrode hanger into the electrode hole at one end, and place the soft cushion under the other end of the electrode to avoid damaging the electrode joint; (see pic1)
3.Use compressed air to blow the dust and sundries on the surface and hole of the connecting electrode, and then clean the surface and connector of the new electrode, clean it with a brush; (see pic2)
4.Lift the new electrode above the pending electrode to align with the electrode hole and fall slowly;
5.Use a proper torque value to properly lock electrode; (see pic3)
6.Clamp holder should be placed out of the alarm line. (see pic4)
7.In the refining period, it is easy to make the electrode thin and cause breaking, joint fall off, increase electrode consumption, please don’t use electrodes to raise carbon content.
8.Due to the different raw materials used by each manufacturer and the manufacturing process, the physical and chemical properties of electrodes and joints of each manufacturer. So in use, under general circumstances, Please don’t mixed use electrodes and joints produced by different manufacturers.

Graphite-Electrode-Instruction


  • Previous:
  • Next:

  • Write your message here and send it to us

    Related products

    • UHP 550mm 22 Inch Graphite Electrode For Electric Arc Furnace

      UHP 550mm 22 Inch Graphite Electrode For Electr...

      Technical Parameter Parameter Part Unit UHP 550mm(22”) Data Nominal Diameter Electrode mm(inch) 550 Max Diameter mm 562 Min Diameter mm 556 Nominal Length mm 1800/2400 Max Length mm 1900/2500 Min Length mm 1700/2300 Max Current Density KA/cm2 18-27 Current Carrying Capacity A 45000-65000 Specific Resistance Electrode μΩm 4.5-5.6 Nipple 3.4-3.8 Flexu...

    • Graphite Electrodes Nipples 3tpi 4tpi Connecting Pin T3l T4l

      Graphite Electrodes Nipples 3tpi 4tpi Connectin...

      Description The graphite electrode nipple is a small but essential part of the EAF steelmaking process. It is a cylindrical-shaped component that connects the electrode to the furnace. During the steelmaking process, the electrode is lowered into the furnace and placed in contact with the molten metal. Electrical current flows through the electrode, generating heat, which melts the metal in the furnace. The nipple plays a crucial role in maint...

    • UHP 600x2400mm Graphite Electrodes for Electric Arc Furnace EAF

      UHP 600x2400mm Graphite Electrodes for Electric...

      Technical Parameter Parameter Part Unit UHP 600mm(24”) Data Nominal Diameter Electrode mm(inch) 600 Max Diameter mm 613 Min Diameter mm 607 Nominal Length mm 2200/2700 Max Length mm 2300/2800 Min Length mm 2100/2600 Max Current Density KA/cm2 18-27 Current Carrying Capacity A 52000-78000 Specific Resistance Electrode μΩm 4.5-5.4 Nipple 3.0-3.6 Flexu...

    • Soderberg Carbon Electrode Paste for  Ferroalloy Furnace  Anode Paste

      Soderberg Carbon Electrode Paste for Ferroallo...

      Technical Parameter Item Sealed Electrode Past Standard Electrode Paste GF01 GF02 GF03 GF04 GF05 Volatile Flux(%) 12.0-15.5 12.0-15.5 9.5-13.5 11.5-15.5 11.5-15.5 Compressive Strength(Mpa) 18.0 17.0 22.0 21.0 20.0 Resisitivity(uΩm) 65 75 80 85 90 Volum Density(g/cm3) 1.38 1.38 1.38 1.38 1.38 Elongation(%) 5-20 5-20 5-30 15-40 15-40 Ash(%) 4.0 6.0 ...

    • Graphite Electrodes For Steel Making High Power HP 16 Inch EAF LF HP400

      Graphite Electrodes For Steel Making High Power...

      Technical Parameter Parameter Part Unit HP 400mm(16”) Data Nominal Diameter Electrode mm(inch) 400 Max Diameter mm 409 Min Diameter mm 403 Nominal Length mm 1600/1800 Max Length mm 1700/1900 Min Length mm 1500/1700 Current Density KA/cm2 16-24 Current Carrying Capacity A 21000-31000 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.5-4.5 Flexural S...

    • Carbon Blocks Extruded Graphite Blocks Edm Isostatic Cathode Block

      Carbon Blocks Extruded Graphite Blocks Edm Isos...

      Technical Parameter Physical And Chemical Indexes For Graphite Block Item Unit GSK TSK PSK Granule mm 0.8 2.0 4.0 Density g/cm3 ≥1.74 ≥1.72 ≥1.72 Resistivity μ Ω.m ≤7.5 ≤8 ≤8.5 Compressive Strength Mpa ≥36 ≥35 ≥34 Ash % ≤0.3 ≤0.3 ≤0.3 Elastic Modulus Gpa ≤8 ≤7 ≤6 CTE 10-6/℃ ≤3 ≤2.5 ≤2 Flexural Strength Mpa 15 14.5 14 Porosity % ≥...