Electric Arc Furnace Graphite Electrodes HP550mm With Pitch T4N T4L 4TPI Nipples
Technical Parameter
|
Parameter |
Part |
Unit |
HP 550mm(22”) Data |
|
Nominal Diameter |
Electrode |
mm(inch) |
550 |
|
Max Diameter |
mm |
562 |
|
|
Min Diameter |
mm |
556 |
|
|
Nominal Length |
mm |
1800/2400 |
|
|
Max Length |
mm |
1900/2500 |
|
|
Min Length |
mm |
1700/2300 |
|
|
Current Density |
KA/cm2 |
14-22 |
|
|
Current Carrying Capacity |
A |
34000-53000 |
|
|
Specific Resistance |
Electrode |
μΩm |
5.2-6.5 |
|
Nipple |
3.2-4.3 |
||
|
Flexural Strength |
Electrode |
Mpa |
≥10.0 |
|
Nipple |
≥22.0 |
||
|
Young’s Modulus |
Electrode |
Gpa |
≤12.0 |
|
Nipple |
≤15.0 |
||
|
Bulk Density |
Electrode |
g/cm3 |
1.68-1.72 |
|
Nipple |
1.78-1.84 |
||
|
C.T.E. |
Electrode |
×10-6/℃ |
≤2.0 |
|
Nipple |
≤1.8 |
||
|
Ash Content |
Electrode |
% |
≤0.2 |
|
Nipple |
≤0.2 |
NOTE:Any specific requirement on dimension can be offered.
Widely Use in Industry
- For Electric arc furnace steel making
- For Yellow phosphorus furnace
- Apply to Industrial silicon furnace or melting copper.
- Apply to Refine steel in ladle furnaces and in other smelting processes
Graphite Electrode Selection
Graphite electrode oxidation is one of the significant factors affecting electrode consumption during EAF steelmaking. When oxidation occurs, the electrode loses its structural integrity, leading to rusting and flaking.
The sublimation and dissolution of graphite electrodes can also lead to considerable consumption rates during EAF steelmaking.
Spalling and breaking of graphite electrodes are also significant consumption factors during EAF steelmaking.
The diameter and length of the graphite electrode are also crucial factors to consider when choosing electrodes for EAF steelmaking.
Graphite Electrode Maintenance
Once you have chosen the right graphite electrode, it's essential to maintain it properly to minimize electrode consumption. Regular inspections and cleaning are necessary to remove any debris or slag buildup on the electrodes, which can increase resistance and reduce efficiency. Additionally, the proper storage of electrodes is vital to maintain their quality. Storage areas must be dry, well-ventilated, and free from contaminating elements such as oil or moisture. It's also essential to handle the electrodes with care to prevent damage during transportation and installation.Proper use and maintenance can effectively reduce graphite electrode consumption.
We are the manufacture owned complete production line and professional team.
For every production processing,we have complete QC system for the chemical composition and Physical properties.After production,all the goods will be tested.We will use the gauge imported from Japan with high-precision measurement between nipple and electrode. We also will inspect other specifications such as resistance, bulk density etc. will be checked and tested by the professional equipment before delivery from our manufacture.
Currently, Gufan mainly produces high quality graphite electrodes including UHP,HP,RP grade,from diameter 200mm(8”) to 700mm(28”).which are capable for using in Electric Arc Furnace. The large diameters, such as UHP700,UHP650 and UHP600, get good feedback from our customers.
Customer Satisfaction Guarantee
Your “One-Stop-Shop” for GRAPHITE ELECTRODE at the guaranteed lowest price
From the moment you contact Gufan, our team of experts are committed to providing outstanding service, quality products, and timely delivery, and we stand behind every product we produce.
Related products
-
Graphite Electrodes In Electrolysis HP 450mm 18...
Technical Parameter Parameter Part Unit HP 450mm(18”) Data Nominal Diameter Electrode mm(inch) 450 Max Diameter mm 460 Min Diameter mm 454 Nominal Length mm 1800/2400 Max Length mm 1900/2500 Min Length mm 1700/2300 Current Density KA/cm2 15-24 Current Carrying Capacity A 25000-40000 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.5-4.5 Flexural S...
-
High Power Graphite Electrode For EAF LF Smelti...
Technical Parameter Parameter Part Unit HP 350mm(14”) Data Nominal Diameter Electrode mm(inch) 350(14) Max Diameter mm 358 Min Diameter mm 352 Nominal Length mm 1600/1800 Max Length mm 1700/1900 Min Length mm 1500/1700 Current Density KA/cm2 17-24 Current Carrying Capacity A 17400-24000 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.5-4.5 Flexur...
-
Graphite Electrodes For Steel Making High Power...
Technical Parameter Parameter Part Unit HP 400mm(16”) Data Nominal Diameter Electrode mm(inch) 400 Max Diameter mm 409 Min Diameter mm 403 Nominal Length mm 1600/1800 Max Length mm 1700/1900 Min Length mm 1500/1700 Current Density KA/cm2 16-24 Current Carrying Capacity A 21000-31000 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.5-4.5 Flexural S...
-
HP24 Graphite Carbon Electrodes Dia 600mm Elec...
Technical Parameter Parameter Part Unit HP 600mm(24”) Data Nominal Diameter Electrode mm(inch) 600 Max Diameter mm 613 Min Diameter mm 607 Nominal Length mm 2200/2700 Max Length mm 2300/2800 Min Length mm 2100/2600 Current Density KA/cm2 13-21 Current Carrying Capacity A 38000-58000 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.2-4.3 Flexural S...
-
Graphite Electrode Manufacturers In China HP500...
Technical Parameter Parameter Part Unit HP 500mm(20”) Data Nominal Diameter Electrode mm(inch) 500 Max Diameter mm 511 Min Diameter mm 505 Nominal Length mm 1800/2400 Max Length mm 1900/2500 Min Length mm 1700/2300 Current Density KA/cm2 15-24 Current Carrying Capacity A 30000-48000 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.5-4.5 Flexural ...
-
Graphite Electrodes With Nipples Manufacturers ...
Technical Parameter Parameter Part Unit HP 300mm(12”) Data Nominal Diameter Electrode mm(inch) 300(12) Max Diameter mm 307 Min Diameter mm 302 Nominal Length mm 1600/1800 Max Length mm 1700/1900 Min Length mm 1500/1700 Current Density KA/cm2 17-24 Current Carrying Capacity A 13000-17500 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.5-4.5 Flexu...